LYT-311C high iron oxide desulfurizer at ambient temperature

The physical properties of the catalysts

Making

The appearance of brown streaks

The specification of 5 x 5 ~ 10mm

The density of kg/L 0.70 ~ 0.85kg/L

Sulfur containing ≥ 30%

Wear loss ≤ 1%

Crushing strength N/cm ≥ 40N / cm

The product features and use: LYT-311C normal temperature ferric oxide desulfurizer is high, with iron as the basic material, chemically synthesized intoactivated ferric oxide desulfurizer, add strip composite additives and adhesiveprocess, the product has the sulfur capacity, small resistance, high degree of purification, good water resistance, used in petroleum refining, coal chemical,organic synthesis, chemical fertilizer industry, to remove the hydrogen sulfide gascity gas and industrial raw materials in chemical fiber etc..

The normal application process conditions:

The purified gas H2S content less than 10ppm for iso.

Pressure: pressure ~ 13.0Mpa

Temperature: room temperature to 110 DEG C

Gas space velocity: 400 ~ 2000h-1

Bed height / diameter: 3

Desulfurizing principle:

Fe2O3 + H2S - FeS + FeSx + H2O

Fe2O3 and H2S, depending upon how much O2 content in gas, can generatedifferent iron sulfides or elemental sulfur.

Transportation and storage:

1 desulfurization agent for making bags, lined with plastic bag.

Avoid scrolling should be 2 in the process of transportation, collision and vibration,so as to avoid crushing.

3 without damaging the packaging case, stored for 3 ~ 5 years normal use.